Please use this identifier to cite or link to this item: http://arks.princeton.edu/ark:/88435/dsp01dj52w482w
 Title: Strained silicon and silicon-germanium quantum devices by chemical vapor deposition Authors: LI, JIUN-YUN Advisors: Sturm, James C Contributors: Electrical Engineering Department Keywords: 2DEGchemical vapor depositionmobilitytunneling Subjects: Electrical engineeringMaterials Science Issue Date: 2013 Publisher: Princeton, NJ : Princeton University Abstract: Strained SiGe band-to-band tunneling (BTBT) devices and strained Si two-dimensional electron gases (2DEGs) are promising for low-power and quantum computing applications. The objective of this dissertation is to pursue the fundamental understanding of BTBT in strained SiGe films and electron transport properties in strained Si. We report the first quantitative study of BTBT in strained p+-SiGe/n+-Si heterojunctions and p+-SiGe/n+-SiGe homojunctions at forward and reverse biases. Negative differential resistance (NDR) at forward bias is clearly observed for each device, with the highest observed peak current density of 104 A/cm2. In reverse bias, a BTBT current density of 106 A/cm2 is measured and a model comparison with good agreement is also presented. Furthermore, we demonstrate that the precise modeling of reverse-biased BTBT devices requires the observation of NDR in forward bias. The surface segregation of phosphorus in relaxed SiGe films is studied with an extremely sharp phosphorus turn-off slope of 6 nm/decade reported. This enables effective Schottky gating on a depletion-mode device of a Si two-dimensional electron gas (2DEG). We also investigate the effect of surface hydrogen on phosphorus segregation. A phenomenological model for this segregation is proposed to explain the experimental results with good agreement. A 2DEG with a record high mobility of 522,000 cm2/V-s in an isotopically enriched 28Si quantum well is presented. The estimated electron dephasing time of ~ 2 μs is presented. We investigate the effects of different layers in a Si 2DEG structure on electron mobility and conclude that the remote impurity charges are the dominant source for electron scattering. The reduced segregation of phosphorus enables an inverted modulation-doped Si 2DEG with extremely high mobility of 470,000 cm2/V-s. For the first time second subband occupancy was achieved in a Si quantum well. URI: http://arks.princeton.edu/ark:/88435/dsp01dj52w482w Alternate format: The Mudd Manuscript Library retains one bound copy of each dissertation. Search for these copies in the library's main catalog Type of Material: Academic dissertations (Ph.D.) Language: en Appears in Collections: Electrical Engineering

Files in This Item:
File Description SizeFormat